Product Details:
| Minimum Order Quantity | 100 Kilogram |
| Form | Powder |
| Usage/Application | Paints |
| Packaging Size | 25 kg |
| Packaging Type | 25 Kgs HPPE bags with liner inside |
| Is it Customized | Yes |
| Country of Origin | Made in India |
|
PROPERTY |
UNIT | VALUE |
|
Whiteness |
-- | 95-98 |
|
Specific surface area |
m2/g |
60-80 |
|
Mean particle size |
mm |
4-6 |
|
Tamped density (after storage) |
g/l |
200-250 |
|
Loss on drying (2 hrs at 105°C) |
% |
5-7 |
|
Loss on Ignition (2 hrs at 1000°C) |
% max |
8 |
|
pH value |
-- |
9.5-10.3 |
|
DBP absorption |
g/100g |
160-180 |
|
SiO2 content |
% |
82 |
|
Al content as Al2 O3 |
% |
9.5 |
|
Na content as Na2O |
% |
8 |
|
Fe content as Fe2 O3 |
%. |
0.03 |
|
Sulfate content as SO3 |
% max |
1.0 |
|
Sieve residue 45 mm |
% max |
0.1 |
|
Packing |
Kg/bag |
25 |
ADVANTAGE OF OUR PRODUCTS IN PAINTS:
Ø Higher degree of whiteness and hiding power of the paint once applied (when dry). Greater development of the degree of whiteness of the white pigments used.
Ø Cost reduction in the formula, especially when titanium dioxide is substituted. Up to 20%-30% in weight of the white pigments used can be substituted.
Ø Increased stability of the paint during storage over long periods. It acts as an anti-settling agent and a regulatory agent of the viscosity and of the pH.
Ø Gives exterior paints good weathering properties and reduces its tendency to dirt pick-up.
Additional Information:
Product Details:
| Minimum Order Quantity | 25 Kilogram |
| Moisture | 1.5 Max |
| Water absorption | 50-60 |
| Residue on 500 mesh % | 2.5 % |
| Colour | Snow white , Free flowing powder |
| Grade | Food and Pharma |
| Heavy Metals | Below 2ppm |
| Bulk Density* | 0.35-0.40 gm/cc |
| Country of Origin | Made in India |
|
Test and Method |
Specification |
|
Identification A(JP) |
The solution responds to the Qualitative Tests for aluminum salt. |
|
Identification B(JP) |
upon cooling, an opaque bead with a web-like structure. |
|
Purity (JP) |
|
|
1. Acidity or alkalinity (JP) |
Shake 1.0g of Synthetic Aluminum Silicate with 20 mL of water, and centrifuge: the supernatant liquid so obtained is neutral. |
|
2. Chloride (JP) |
Not More than 0.021 % |
|
3. Sulfate (JP) |
Not More than 0.480 % |
|
4. Heavy metals (JP) |
Not More than 30 ppm |
|
5.Arsenic(JP) |
Not More than 2.0 ppm |
|
Loss on drying (1g, 105°C, 3 hours). (JP) |
Not more than 20.0% |
|
Acid-consuming capacity (JP) |
The volume of 0.1 mol/L hydrochloric acid VS consumed is not less than 50.0 mL per g of Synthetic Aluminum Silicate. |
Additional Information: